CAS No.: | 9002-88-4 |
---|---|
Formula: | (C2 H4)N |
EINECS: | 9003-07-0 |
Molecular Principal Chain: | Carbon Chain Polymer |
Color: | White |
Transport Package: | Woven Bag |
Customization: |
---|
Suppliers with verified business licenses
Process mothod
|
Film grade, Injection molding grade, Blowing molding grade, extrusion grade
|
Features
|
·Good surface ·High impact ·High stiffness
|
Applications
|
·Toys ·Bottles ·Housewares application
|
Package
|
25kg per bag
|
Key Properties |
|
---|---|
Density | 0.954 g/cm3 |
Melt Index (g/10min @190°C/2.16 kg (ASTM D1238)) | 20 |
Application Benefits |
|
---|---|
Anti-block | No |
Closure Type | Caps |
Slip | No |
Typical Properties |
|
---|---|
2% Secant Modulus, MD (ASTM D882) in MPa (psi) | 1150 (167000) |
2% Secant Modulus, TD (ASTM D882) in MPa (psi) | 1150 (167000) |
Brittleness Temperature in °C(°F) | < -76.1 |
Density Range | .951-.960 |
ESCR-Environmental Stress Crack Resistance (100% IGEPAL) | 3 hr |
Fabrication Method | Injection Molding |
Functionality | Mechanical Performance |
Impact Strength in MPa (psi) | 42 kJ/m2 (20 ft lb/in2) ASTM D1822 |
Tensile Elongation at Break, MD | 250 % |
Tensile Elongation at Break, TD | 250 % |
Tensile Strength Break, MD (ASTM D638) in MPa (psi) | 13.8 (2000) |
Tensile Strength Break, TD (ASTM D638) in MPa (psi) | 13.8 (2000) |
Tensile Strength Yield, MD (ASTM D638) in MPa (psi) | 28.3 (4100) |
Tensile Strength Yield, TD (ASTM D638) in MPa (psi) | 28.3 (4100) |
Packing Details : Standard Packing(25KG/Bag.1MT/Bag.Or as your requirements.)
Delivery Details : 5-10 days after order
Inner (Plastic film)
Outer(Paper bag or woven bag)
Supply Ability:100,000 Ton/Tons per Mont
Suppliers with verified business licenses